ET514 A side

ET514 B side

Chemical

composition

Epoxy Resin

Polyamine Hardener

Appearance

White

Black

Viscosity @ 25°C

20rpm: 65,000

mPa.s (cP)

2rpm: 225,000

mPa.s (cP)

20rpm: 65,000

mPa.s (cP)

2rpm: 150,000

mPa.s (cP)

Specific gravity

1.1

1.2

Mix ratio by volume

1:1

Maximum gap fill

2 mm 0.08 in

Usable / pot life @23°C

30-50 mins

Handling time @23°C

60-120 mins

Working strength @23°C

8-12 hours

Full cure @23°C

24 hours

Shear strength* (ISO4587)

Mild steel: 20-30 N/mm²

(2900-4350psi)

Aluminium: 12-16 N/mm²

(1740-2320psi)

Stainless Steel: 18-22 N/mm²

(2610-3190psi)

Carbon Fibre: 17-21 N/mm²

(2465-3045psi)

FRP Glass/Polyester: >12 N/mm²** SF

(>1740psi)

FRP Glass/Epoxy: 17-21 N/mm²

(2465-3045psi)

PEEK: 3-4 N/mm²

(435-580psi)

Polycarbonate: >8 N/mm²** SF

(>1160psi)

PA6 30% filled: 6-7 N/mm²

(870-1015psi)

PA6 unfilled: 3-4 N/mm²

(435-580psi)

Peel strength (aluminium)

(ISO11339)

100-150 N/25mm (23-34 PIW)

Hardness

(ISO868)

60-75 Shore D

Elongation at

break (ISO37)

10-15%

Glass transition temperature Tg

40-50°C (104-122°F)

Dielectric

strength

15-25 kV/ mm

Thermal

conductivity

0.3 W/(m.K)