PERMABOND® ET514 is a 1:1 mixable epoxy adhesive. It has excellent resistance to impact and vibration and is ideal for structural bonding of metal, wood, composites and certain plastics. Its rapid cure speed coupled with its structural strength makes this adhesive suitable for a wide variety of applications. ET514 is high strength and has excellent environmental durability.

FEATURES AND BENEFITS

  • Adhesion to a wide variety of substrates     
  • Full cure at room temperature
  • Easy to apply
  • High shear and peel strength     
  • Good impact strength

Physical Properties of Uncured Adhesive

 

 

ET514 A side

ET514 B side

Chemical

composition

Epoxy Resin

Polyamine Hardener

Appearance

White

Black

 

Viscosity @ 25°C

20rpm: 65,000

mPa.s (cP)

2rpm: 225,000

mPa.s (cP)

20rpm: 65,000

mPa.s (cP)

2rpm: 150,000

mPa.s (cP)

Specific gravity

1.1

1.2

 

Typical Curing Properties

Mix ratio by volume

1:1

Maximum gap fill

2 mm 0.08 in

Usable / pot life @23°C

30-50 mins

Handling time @23°C

60-120 mins

Working strength @23°C

8-12 hours

Full cure @23°C

24 hours

Typical Performance of Cured Adhesive

 

 

 

 

 

 

 

 

 

 

Shear strength* (ISO4587)

Mild steel: 20-30 N/mm²

(2900-4350psi)

Aluminium: 12-16 N/mm²

(1740-2320psi)

Stainless Steel: 18-22 N/mm²

(2610-3190psi)

Carbon Fibre: 17-21 N/mm²

(2465-3045psi)

FRP Glass/Polyester: >12 N/mm²** SF

(>1740psi)

FRP Glass/Epoxy: 17-21 N/mm²

(2465-3045psi)

PEEK: 3-4 N/mm²

(435-580psi)

Polycarbonate: >8 N/mm²** SF

(>1160psi)

PA6 30% filled: 6-7 N/mm²

(870-1015psi)

PA6 unfilled: 3-4 N/mm²

(435-580psi)

Peel strength (aluminium)

(ISO11339)

 

100-150 N/25mm (23-34 PIW)

Hardness

(ISO868)

60-75 Shore D

Elongation at

break (ISO37)

10-15%

Glass transition temperature Tg

40-50°C (104-122°F)

Dielectric

strength

15-25 kV/ mm

Thermal

conductivity

0.3 W/(m.K)

TDS:Download

Get MSDS

    Leave your information via Form, our Technical Support Team will contact you shortly!

    YINCAE Solder Joint Encapsulants SMT 266
    YINCAE Solder Joint Encapsulants SMT 266
    https://prostech.vn/yincae-solder-joint-encapsulants-smt-266/

    Key Features of YINCAE Solder Joint Encapsulants SMT 266Applications for YINCAE Solder Joint Encapsulants SMT 266 Introducing YINCAE Solder Joint

    YINCAE Solder Joint Encapsulants SMT 256
    YINCAE Solder Joint Encapsulants SMT 256
    https://prostech.vn/yincae-solder-joint-encapsulants-smt-256/

    Elevate Reliability with YINCAE Solder Joint Encapsulants SMT 256Key Features & BenefitsApplications of YINCAE Solder Joint Encapsulants SMT 256 YINCAE

    YINCAE Solder Joint Encapsulants SMT 256 BC
    YINCAE Solder Joint Encapsulants SMT 256 BC
    https://prostech.vn/yincae-solder-joint-encapsulants-smt-256-bc/

    Why Choose YINCAE Solder Joint Encapsulants SMT 256 BC?Key Applications YINCAE Solder Joint Encapsulants SMT 256 BC is a cutting-edge

    YINCAE Solder Joint Encapsulants SMT 138
    YINCAE Solder Joint Encapsulants SMT 138
    https://prostech.vn/yincae-solder-joint-encapsulants-smt-138/

    Key Features of YINCAE Solder Joint Encapsulants SMT 138Versatile Applications YINCAE Solder Joint Encapsulants SMT 138 is a cutting-edge, low-temperature