PERMABOND ET5393 Keo Epoxy Hai Thành Phần

ET5393A

ET5393B

Chemical

composition

Epoxy Resin

Phenalkamine

Appearance

Blue paste

Yellow paste

Viscosity @ 23°C

20rpm: 120,000-

180,000 mPa.s (cP)

2rpm: 500,000-

650,000 mPa.s (cP)

20rpm: 70,000-

130,000 mPa.s (cP)

2rpm: 200,000-

350,000 mPa.s (cP)

Specific

gravity

1.1

1.05

Mix ratio

1:1 by volume

100:90 by weight

Maximum gap fill

2 mm 0.08 in

Usable / pot life @23°C 10g mixed

15-25 mins

Handling time @23°C

2-3 hours

Working strength @23°C

8 hours

Full cure

@23°C: 24 hours

@60°C: 1 hour

Shear strength (mild steel)* (ISO4587)

Cured 24 hrs @23°C: 18-20 N/mm²

(2600-2900 psi)

Cured 1 hr @ 60°C: 20-23 N/mm²

(2900-3300 psi)

Shear strength (stainless steel)* (ISO4587)

Cured 24 hrs @ 23°C

As received: 16-20 N/mm² (2300-2900 psi)

Gritblast/degrease: 19-22 N/mm²

(2800-3200 psi)

Cured 1 hr @ 60°C

As received: 21-25 N/mm² (3000-3600 psi)

Gritblast/degrease: 23-26 N/mm²

(3300-3800 psi)

Peel strength (aluminium) (ISO4578)

Cured 1hr @ 60°C: 210-230 N/25mm

(46-50 PIW)

Cured 5 days @ 23°C: 180-200 N/25mm

(33-44 PIW)

Hardness

(ISO868)

68-72 Shore D