PERMABOND® ET5429 is a thixotropic two-part adhesive with excellent resistance to impact and vibration. The controlled flow properties as well as its ease of mixing and application, enables the adhesive to be used where gap filling or vertical application is required. Permabond® ET5429 has been found to provide exceptional performance even at elevated temperatures. It is ideal for use in construction of composite assemblies.

FEATURES AND BENEFITS

  • Ideal for bonding composite materials     
  • Easy to apply
  • High shear and peel strength     
  • Good impact strength
  • High temperature resistance

Physical Properties of Uncured Adhesive

 

ET5429 A side

ET5429 B side

Chemical

composition

Epoxy Resin

Polyamine

Hardener

Appearance

White

Black

Mixed appearance

Charcoal black

 

Viscosity @ 25°C

20rpm: 200,000

mPa.s (cP)

2rpm: 300,000 mPa.s

(cP)

20rpm: 60,000

mPa.s (cP)

2rpm: 150,000

mPa.s (cP)

Specific gravity

1.0

1.0

Typical Curing Properties

Mix ratio

2:1 by volume

2:1 by weight

Maximum gap fill

5 mm 0.2 in

Usable / pot life @23°C 10g mixed

2-4 hours

Handling time

23°C: 6-10 hours

Working strength

23°C: 24 hours

60°C: 1 hour

Full cure

23°C: 72 hours

60°C: 2 hours

Typical Performance of Cured Adhesive

 

 

 

 

 

 

 

 

 

Shear strength* (ISO4587)

Mild Steel: 23-28 N/mm²

(3335-4060psi)

Aluminium: 26-31 N/mm²

(3770-4495psi)

Stainless Steel: 25-30 N/mm²

(3625-4350psi)

Carbon Fibre: >25 N/mm² ** SF

(>3625psi)

FRP Glass/Polyester: >6 N/mm²** SF

(>870psi)

FRP Glass/Epoxy: 18-22 N/mm²

(2610-3190psi)

PEEK: 4-5 N/mm²

(580-725psi)

PA6 30% filled: 4-6 N/mm²

(580-870psi)

PVC: >3 N/mm² ** SF

(>435psi)

Polycarbonate: 3-4 N/mm²

(435-580psi)

Peel strength (aluminium)

(ISO4578)

 

150-230 N/25mm (33-51 PIW)

Impact strength

(ASTM D-950)

30-40 KJ/m²

Hardness

(ISO868)

65-75 Shore D

Elongation at break (ISO37)

<5%

Glass transition

temperature Tg

50-60°C (122-140°F)

Dielectric

strength

15-25 kV/ mm

TDS:Download

Get MSDS

    Leave your information via Form, our Technical Support Team will contact you shortly!

    YINCAE Solder Joint Encapsulants SMT 266
    YINCAE Solder Joint Encapsulants SMT 266
    https://prostech.vn/yincae-solder-joint-encapsulants-smt-266/

    Key Features of YINCAE Solder Joint Encapsulants SMT 266Applications for YINCAE Solder Joint Encapsulants SMT 266 Introducing YINCAE Solder Joint

    YINCAE Solder Joint Encapsulants SMT 256
    YINCAE Solder Joint Encapsulants SMT 256
    https://prostech.vn/yincae-solder-joint-encapsulants-smt-256/

    Elevate Reliability with YINCAE Solder Joint Encapsulants SMT 256Key Features & BenefitsApplications of YINCAE Solder Joint Encapsulants SMT 256 YINCAE

    YINCAE Solder Joint Encapsulants SMT 256 BC
    YINCAE Solder Joint Encapsulants SMT 256 BC
    https://prostech.vn/yincae-solder-joint-encapsulants-smt-256-bc/

    Why Choose YINCAE Solder Joint Encapsulants SMT 256 BC?Key Applications YINCAE Solder Joint Encapsulants SMT 256 BC is a cutting-edge

    YINCAE Solder Joint Encapsulants SMT 138
    YINCAE Solder Joint Encapsulants SMT 138
    https://prostech.vn/yincae-solder-joint-encapsulants-smt-138/

    Key Features of YINCAE Solder Joint Encapsulants SMT 138Versatile Applications YINCAE Solder Joint Encapsulants SMT 138 is a cutting-edge, low-temperature