VieTape FS5701 ENHANCED SEALABILITY

PROPERTY

TEST METHOD

VALUE

PHYSICAL

Density, kg /m3 (lb. / ft3)

Tolerance, %

ASTM D 3574-95, Test A

240 (15)

320 (20)

480 (30)

± 10

Thickness, mm

(inches)

4.78 – 12.70

(0.188-0.500)

1.57 – 3.18

(0.062- 0.125)

0.79 – 1.14

(0.031-0.045)

Tolerance, %

± 10

± 20

Standard Color (Code)

Black (04)

Compression Force Deflection, kPa

(psi)

Typical, kPa (psi)

0.51 cm/min (0.2” / min.) Strain Rate

41 – 83

76 – 138

138 – 317

Force Measured @25% Deflection

(6 – 12)

64 (9.3)

(11 – 20)

103 (15)

(20 – 46)

193 (28)

Hardness, Durometer, Shore “O”

ASTM D 2240-97

18

24

55

Compression Set, % max. after 24

ASTM D 3574-95

5

hour recovery

Test D @23oC(73oF) ASTM D 3574-95

10

Test D @70oC (158oF)

5

ASTM D 3574-95 Test J/Test D

autoclaved 5 hrs @121oC (250oF)

Dimensional Stability, % max. change

22 hrs @80oC (176oF) in a forced-air oven

± 2

Tensile Strength, min. kPa (psi)

ASTM D 3574-75 Test E

276 (40)

517 (75)

827 (120)

Tensile Elongation, % min.

ASTM D 3574-75 Test E

100

100

100

Tear Strength, Min. kN/m (pli),

ASTM D 264-91 Die C

1.1 (6)

1.4 (8)

2.6 (15)

Typical kN/m (pli)

1.8 (10)

2.3 (13)

3.2 (18)

ELECTRICAL   AND THERMAL

Dielectric Constant, K’ (“DK”)

ASTM D 150 measurements at 22oC (72oF) relative humidity 50% for 24 hrs.

1.71

Dielectric Strength, kVm (volts/mil)

ASTM D 149-97a

1969 (50)

Dissipation Factor, tan D (“DF”)

ASTM D 150-98

0.05

Volume Resistivity, ohm-cm

ASTM D 257-99

1 x 1012

Surface Resistivity, ohm/sq.

ASTM D 257-99

2 x 1012

Thermal Conductivity, W/m-C

(BTU-in./hr/ft2-F)

ASTM C 518-98

–

–

–

Coefficient of Thermal Expansion

2.3-3.1 x 10-4 in/in/oC (1.3-1.7×10-4in/in/oF)

TEMPERATURE RESISTANCE

Recommended Constant Use, max.

SAE J-2236

90oC (194oF)

Recommended Intermittent Use, max.

121oC (250oF)

Embrittlement

ASTM D 746-98

–

Cold Flexibility

MIL-P-12420D 1991 @-40oC (-40oF)

Pass

FLAMMABILITY AND OUTGASSING

Flammability, mm (inches)

UL 94HBF (File E20305) (Pass ≥)

4.8 (0.188)

MVSS 302 (Pass ≥)

–

CSA Comp HBF(File 188149) (Pass ≥)

–

Fogging

SAE J-1756 3 hrs @100oC (212oF)

–

Outgassing, Total Mass Loss (TML) %

ASTM E 595-93 24 hrs @125oC (257oF) @

<7×103 Pa

0.84

0.97

1.0

Outgassing, Collected Volatile Condensable Materials (CVCM) %

0.05

0.04

0.06

Outgassing, Water Vapor Regain (WVR) %

0.4

0.46

0.65

ENVIRONMENTAL

Gasketing and Sealing

UL JMST2 (Consisting of UL50 and UL508) CAN/CSA – C22.2 No. 94-M91

File MH15464 File 188149

Moisture Absorption, High Humidity Exposure, % weight gain, typical

AMS 3568-95

3

Water Absorption, Immersion Testing,

% weight gain, typical

ASTM D 570-95

15

13

6

UV Resistance

ASTM G 53-96

–

Ozone Resistance

GM 4486P-95

–

Corrosion Resistance

AMS 3568-91

–

Mildew/Bacteria Resistance

ASTM G 21

Good

Staining

ASTM D 925

No Stain

Skin Contact Irritation

Primary Skin Irritation Test (FHSA)

Pass