ET5392A

ET5392B

Chemical

composition

Epoxy Resin

Polyamide

Appearance

White

Black

Viscosity @ 23°C

2rpm: 500,000-750,000

20rpm: 140,000-

180,000 mPa.s (cP)

20rpm: 30,000-

50,000 mPa.s (cP)

Specific gravity

1.1

1.3

Mix ratio

1:1 by volume

95:100 by weight

Maximum gap fill

4 mm 0.08 in

Usable / pot life @23°C 10g mixed

2 hours

Handling time @23°C

8-12 hours

Working strength @23°C

24 hours

Full cure

@23°C: 72 hours

@60°C: 2 hours

Shear strength (mild steel)* (ISO4587)

Cured 72hrs @23°C: 22-24 N/mm²

(3200-3500 psi)

Cured 2 hrs @ 60°C: 23-25 N/mm²

(3300-3600 psi)

Shear strength (stainless steel)* (ISO4587)

Cured 72 hrs @ 23°C

As received: 23-26 N/mm² (3300-3800 psi)

Gritblast/degrease: 26-28 N/mm²

(3800-4000 psi)

Cured 2 hrs @ 60°C

As received: 23-26 N/mm² (3300-3800 psi)

Gritblast/degrease: 30-33 N/mm²

(4400-4800 psi)

Peel strength (aluminium)

(ISO4578)

Cured 2hrs @ 60°C: 100-110 N/25mm

(22-24 PIW)

Hardness (ISO868)

72-76 Shore D