ET5143A

ET5143B

Chemical

composition

Epoxy Resin

Polyamine

Hardener

Appearance

White

Black

Viscosity @ 25°C

20rpm: 50,000-

80,000 mPa.s (cP)

2rpm: 200,000-

300,000 mPa.s

(cP)

20rpm: 100,000-

200,000 mPa.s (cP)

2rpm: 200,000-

300,000 mPa.s (cP)

Specific gravity

1.3

1.3

Mix ratio by volume

1:1

Maximum gap fill

2 mm 0.08 in

Usable / pot life @23°C 1+1g

60-80 mins

Handling time @23°C

3-5 hours

Working strength

@23°C: 16 hours

@60°C: 30

minutes

Full cure

@23°C: 72 hours

@60°C: 1 hour

Shear strength* (ISO4587)

Mild steel: 18-22 N/mm²

(2600 -3200 psi)

Stainless steel: 12-15 N/mm²

(1750 -2200 psi)

Aluminium: 10-14 N/mm²

(1450 -2000 psi)

Peel strength (aluminium)

(ISO4578)

30-50 N/25mm (7-11 PIW)

Hardness (ISO868)

>75 Shore D

Glass transition

temperature Tg

40-50°C (104-122°F)

Dielectric strength

15-25 kV/ mm