Product Description
Devcon® Carbide Putty (product code: 10050, 10080) is a silicon carbide-filled epoxy putty designed to provide economical protection against wear and abrasion. It is ideal for applications that involve handling particulate less than 1/16″ (1.6mm), such as pipe elbows, pulverizers, slurry lines, cyclones, and exhaust fans.
Features of Devcon® Carbide Putty
- Silicon carbide-filled epoxy putty for wear and abrasion resistance
- Non-sagging and extremely wear-resistant
- Room temperature cure for convenience
- Handles particulate less than 1/16″ (1.6mm)
- Withstands continuous service temperatures up to 250ºF
- Open Time: 50 minutes
- Gap Fill: 0.25″ – 1.5″+
Applications of Devcon® Carbide Putty
- Ideal for pipe elbows, pulverizers, and slurry lines
- Suitable for cyclones and exhaust fans
- Provides protection in environments involving aggressive industrial conditions
- Used for applications that require high abrasion resistance and handling of small particulates
Prostech offers specialty materials (adhesives, tapes, thermal interface materials, insulating materials, sealants, PCB protection materials, …) along with manufacturing solutions. We proudly serve a wide range of industries and are an authorized distributor for leading global manufacturers of industrial materials and equipment. Our product range is designed to deliver customized solutions that address each customer’s unique needs. With years of experience and a successful project history, we are confident in our ability to provide comprehensive material solutions. These solutions effectively tackle the challenges manufacturers face. To explore our full product catalog, simply click here. Our dedicated team is ready to assist with: Moreover, Prostech ensures the safe and accurate global delivery of all materials, including “dangerous goods”, in compliance with legal regulations. For personalized technical support or to receive a quotation, please contact us today.About Prostech
| Property | Typical Value | Units | Test Method |
|---|---|---|---|
| Cured 7 Days @ 75°F (24°C) | |||
| Adhesive Tensile Shear | 1,350 psi (9.3 MPa) | psi (MPa) | ASTM D1002 |
| Coefficient of Thermal Expansion | 14 in/in/°F (25.2 cm/cm·°C) | in/in/°F (cm/cm·°C) | ASTM D696 |
| Compressive Strength | 8,160 psi (56.3 MPa) | psi (MPa) | ASTM D695 |
| Cured Shrinkage | 0.0009 in/in (0.0009 cm/cm) | in/in (cm/cm) | ASTM D2566 |
| Dielectric Constant | 25 | ASTM D150 | |
| Flexural Strength | 5,480 psi (37.8 MPa) | psi (MPa) | ASTM D790 |
| Hardness | 85 Shore D | Shore D | ASTM D2240 |
| Solids by Volume | 100% | % | |
| Temperature Resistance | Wet: 120°F (49°C), Dry: 250°F (121°C) | °F (°C) | |
| Tensile Strength | 2,640 psi (18.2 MPa) | psi (MPa) | ASTM D638 |
| Uncured Properties @ 72°F (23°C) | |||
| Color | Grey | ||
| Coverage (1/4″ / 6.35mm) | 64 in²/lb (910 cm²/kg) | in²/lb (cm²/kg) | |
| Functional Cure | 16 hrs | hrs | |
| Mix Ratio by Volume | 4:1 | ||
| Mix Ratio by Weight | 8:1 | ||
| Mixed Viscosity | Putty | ||
| Pot Life | 16 hrs | hrs | |
| Recoat Time | 3-6 hrs | hrs | |
| Specific Gravity | 1.46 lb/gal (1.75 g/cm³) | lb/gal (g/cm³) | |
| Volume | 15.9 in³/lb (0.574 cm³/g) | in³/lb (cm³/g) |