3M™ Low VOC Double Coated Tape 9599 has a non-woven tissue carrier with acrylic adhesive on both sides. It provides high adhesion to a wide variety of materials and is suitable for automobile interior applications

FEATURES

• VOC analysis (micro g / pcs): measured at external organization which is approved by

Formaldehyde: 0.07

Acetaldehyde: 0.07

Toluene: 0.11

Xylene: 0.02 Ethylbenzene: ND Stylene: ND Tetradecane: 0.03 Dibutyl phthalate: ND

Di-2-ethylhexyl phthalate: ND

Sample Size: 80mm x 100mm/pcs

Dwell Temp: 149°F (65°C)

Dwell Time: 120 minutes

Gas trapping volume: 4L with Tedlar bag

Absorption pipe: Tenax-TA, DNPH cartridge

Absorb air in tedlar bag with each absorption pipe after heating and measure with gas chromatograph mass spectrometer or high speed liquid chromatograph.

APPLICATIONS

• Bond strength is dependent upon the amount of adhesive-to-surface contact developed. Firm application pressure helps develop better adhesive contact and improve bond strength. 15 psi momentary pressure is typical.
• Ideal tape application temperature range is 70°F to 100°F (21°C to 37°C). Initial tape application to surface at temperatures below 50°F (10°C) is not recommended because the adhesive becomes too firm to adhere readily. However, once applied, low temperature holding is generally satisfactory. Surfaces should be clean and dry prior tobonding. We recommend a final surface cleaning with a mixture of 50% isopropyl alcohol and water.