LiPOLY AT900A is a thermally conductive tape. With a fiberglass reinforced layer and a thermal conduc- tivity of 0.9 W/m*K this product is designed for applications where additional durability is needed. AT900A can be provided in either standard sheets or custom-die cuts.
FEATURE
- Thermal conductivity:0.9 W/m*K
- Excellent adhesive properties
- Designed for manufacture
- Excellent long term reliability
- Fiberglass reinforced layer
APPLICATION
- Automotive electronics
- Telecommunications
- LED light bar & LED lamp
- Between any heat-generating component and heat sink
- 5G base station & infrastructure
- EV electric vehicle
PROPERTY |
AT900A |
TEST METHOD |
UNIT |
|
Color |
White |
Visual |
– |
|
Reinforced layer |
Fiberglass |
– |
– |
|
Thickness |
0.15 |
0.25 |
ASTM D374 |
mm |
Density |
1.6 |
1.6 |
ASTM D792 |
g/cm³ |
Application temperature |
-60~120 |
-60~120 |
– |
°C |
Short time temp. @30sec |
200 |
200 |
– |
°C |
ROHS |
Compliant |
Compliant |
– |
– |
ADHESION |
||||
Initial tack |
10 |
8 |
PSTC-6 |
cm |
Lap shear strength |
60 |
60 |
ASTM D1002 |
N/cm² |
Die shear strength@25°C |
107 |
94 |
– |
N/cm² |
Die shear strength@80°C |
70 |
70 |
– |
N/cm² |
Holding power 1kg @25°C |
>10000 |
>10000 |
PSTC-7 |
min |
Holding power 1kg @80°C |
>10000 |
>10000 |
PSTC-7 |
min |
90° Peeling strength @ 25°C, 72 hrs |
>10 |
>12 |
ASTM D3330 |
N/inch |
90° Peeling strength @ Thermal aging |
>14 |
>20 |
80°C 1000 hrs |
N/inch |
90° Peeling strength @ HAST |
>20 |
>25 |
85°C/85%RH 1000 hrs |
N/inch |
90° Peeling strength @ Thermal cycling |
>15 |
>20 |
-40°C~120°C 500 cycles |
N/inch |
ELECTRICAL |
||||
Dielectric breakdown |
2 |
3 |
ASTM D149 |
KV |
Surface resistivity |
>10¹⁰ |
>10¹⁰ |
ASTM D257 |
Ohm |
Volume resistivity |
>10¹⁰ |
>10¹⁰ |
ASTM D257 |
Ohm-m |
THERMAL |
||||
Thermal conductivity |
0.9 |
0.9 |
ASTM D5470 |
W/m*K |
Thermal impedance@5psi |
0.87 |
1.15 |
ASTM D5470 |
°C-in²/ W |
Thermal impedance@10psi |
0.85 |
1.14 |
ASTM D5470 |
°C-in²/ W |
Thermal impedance@15psi |
0.82 |
1.12 |
ASTM D5470 |
°C-in²/ W |