PERMABOND® 943 is a low odour, non-fogging, non- frosting alkoxyethyl cyanoacrylate. The reduced odour improves worker comfort. Unsightly fogging adjacent to bondlines, common with other cyanoacrylate adhesives on hot and humid days, is eliminated. The elimination of fogging improves the production rate of acceptable parts as well as their appearance. The adhesive is very stable and will provide optimum performance for one year when refrigerated.
FEATURES AND BENEFITS
- Low odour for improved worker comfort
- Non-frosting –good aesthetic appearance
- Ease of use – no mixing or heat cure
- Bonds most materials
- 100% reactive, no solvents
Physical Properties of Uncured Adhesive
Chemical composition | Alkoxyethyl cyanoacrylate |
Appearance | Colourless |
Viscosity @ 25°C | 90-110 mPa.s (cP) |
Specific gravity | 1.1 |
Typical Curing Properties
Maximum gap fill | 0.15 mm 0.006 in |
Fixture / handling time* (0.3 N/mm² shear strength is achieved) | 5-10 seconds (PVC) 5-10 seconds (Phenolic resin) 5-10 seconds (ABS) <5 seconds (Neoprene / NBR) 10-15 seconds (Steel) 10-15 seconds (Aluminium) 30-40 seconds (Zinc) |
Full strength | 24 hours |
Typical Performance of Cured Adhesive
Shear strength* (ISO4587) | Steel 16-20 N/mm² (2300-2900 psi) Aluminium 8-9 N/mm² (1200-1300 psi) Zinc 8 N/mm² (1200 psi) ABS >6 N/mm² (900psi) SF** PC >5 N/mm² (700 psi) SF** Phenolic 4 N/mm² (600psi) |
Impact Strength (ASTM D-950) | 3-5 kJ/m² (1.4-2.4 ft-lb/in²) |
Dielectric Strength (DIN 53481) | 25 kV/mm |
Dielectric Constant @ 1MHz (DIN 53483) | 3 |
Hardness (ISO868) | 85 Shore D |
Coefficient of thermal expansion | 90 x 10-6 mm/mm/°C |
Coefficient of thermal conductivity | 0.1 W/(m.K) |