A polyimide film has ultra-high temperature performance. This label product with acrylic adhesive can withstand up to 232oC short-term heat resistance, has excellent solvent resistance and exhibits low outgassing characteristics.
KEY FEATURES
- Matte white thermal transfer topcoat for easy readability of barcodes and variable information
- Adhesive will not degrade when exposed to a wide variety of harsh processing This adhesive also offers exceptional shear strength even at elevated temperatures.
- 50# densified kraft liner assures consistent did-cutting
- UL Recognized file MH16411
Physical Properties |
|
Liner |
50# Densified Kraft |
Liner Thickness |
0.076 mm |
Adhesive Type |
100% Acrylic |
Adhesive Thickness |
0.051 mm |
Facestock |
Polyimide Film and Matte White Kraft Thermal Transfer Printable Topcoat |
Facestock Thickness |
Polyimide Film: 0.051 mm Matte White Kraft Thermal Transfer Printable Topcoat: 0.025 mm |
Die-Cutting |
Rotary die-cutting is recommended |
Performance Characteristics |
|
180° Peel Adhesion (Stainless Steel) (23oC, 50%RH) |
3.5 N/cm |
180° Peel Adhesion (PC) (23oC, 50%RH) |
3.7 N/cm |
180° Peel Adhesion (Epoxy PC Board) (23oC, 50%RH) |
4.8 N/cm |
Performance Characteristics |
|
Chemical and Environmental Exposure |
The properties defined are based on four hour immersions at room temperature (22°C) unless otherwise noted. Samples were applied to stainless steel panels 24 hours prior to immersion and were evaluated one hour after removal from the solution for peel adhesion. Adhesion measured at 180° peel angle (ASTM D 3330) at 12 inches/minute. |
Humidity Resistance |
24 hours at 100°F (38°C) and 100% relative humidity: no significant change in appearance or adhesion. |
Temperature Resistance |
277°C for 30 seconds: no significant visual change 260°C for 7 minutes: slight browning -40°C for 24 hours: no significant visual change |