LOCTITE® AA 3081™ is designed for bonding cannulae into hubs, syringes and lancets. LOCTITE® AA 3081™ has excellent adhesion to glass, metal and certain thermoplastic substrates. The ability of this product to flouresce under black light facilitates inspection of bonded assemblies for adhesive. The low viscosity of this product makes it ideal for applications where wicking of the adhesive into pre-assembled parts is desired. Suitable for use in the assembly of disposable medical devices.
FEATURES
- Fast surface cure
- Fluoresces for quality monitoring
- Also used for metals and ceramics
- Ideal for glass and plastics
- ISO 10993 qualified
APPLICATION
Bonding
|
Technology |
Acrylic |
|
Chemical Type |
Modified acrylate |
|
Appearance (uncured) |
Transparent liquidLMS |
|
Fluorescence |
Positive under UV lightLMS |
|
Components |
One component – requires no mixing |
|
Viscosity |
Low |
|
Cure |
Ultraviolet (UV) light |
|
Cure Benefit |
Production – high speed curing |
|
Application |
Bonding |
TYPICAL PROPERTIES OF UNCURED MATERIAL
| Specific Gravity @ 25 °C | 1.01 |
| Flash Point- See SDS | |
| Infrared Spectroscopy | To match standardLMS |
| Viscosity, Cannon Fenske, ISO 3104, mPa·s (cP) | 70 to 140LMS |
TYPICAL PROPERTIES OF CURED MATERIAL
| Refractive Index | 1.5 | |
| Shore Hardness, ISO 868, Durometer D | 74 | |
| Elongation, at yield, ISO 527-3, % | 3.3 | |
| Elongation, at break, ISO 527-3, % | 7.6 | |
| Tensile Strength, at yield, ISO 527-3 | N/mm² (psi) | 32,4 (4,700) |
| Tensile Strength, at break, ISO 527-3 | N/mm² (psi) | 22.1 (3,200) |
| Tensile Modulus, ISO 527-3 | N/mm² (psi) | 1,875 (272,000) |